银合金粉末粒度对Ag-MoS2复合材料摩擦磨损性能的影响
- 文件大小:1.6MB
- 浏览次数:
- 发布时间:2014-03-16
本资料包含pdf文件1个,下载需要1积分
The Ag-MoS2 composites were prepared by powder metallurgy method. The effects of the atomized Ag-Cu alloy particle size on the microstructure, mechanical properties and tribological performances of composites were investigated. The results show that the dispersion of MoS2 particle in matrix and the mechanical properties of composites are dramatically improved by reducing the particle size of alloy powder. The composite has a low and stable friction coefficient when the small size alloy particle is used. When the particle size of alloy powder is above 38 pro, the wear loss of the composite increases severely. SEM observation indicates that the worn surface is covered with smeared MoS2 particles and discontinuous lubricating film is formed on it. The area of lubricating film covered on the worn surface increases with increasing the homogeneity of MoS2 in the matrix, and a large area of lubricating film can reduce the magnitude of shear stress transferred to subsurface and prevent the metal-to-metal contact. Therefore, it helps to reduce the friction and wear of composite.采用粉末冶金热压的方法制备Ag-MoS2复合材料,研究银合金粉末的粒度对复合材料的组织结构、力学性能和摩擦磨损性能的影响。结果表明:随着银合金粉末粒度的减小,MoS2团聚体在基体中的分散性得到改善,材料的硬度和抗弯强度同时也得到大幅提高。银合金粉末较小时,复合材料的稳定摩擦因数较低且较平稳;当粉末粒径大于38μm时,复合材料的磨损量显著增大。MoS2团聚体弥散的涂覆在磨损表面上形成了不连续的润滑膜,提高MoS2在基体的分散性有利于增加润滑膜在磨损表面的覆盖面积,从而减轻表层材料的剪切应力和减少金属与金属之间的接触,降低材料的摩擦与磨损。
- 1AutoCAD经典实用技巧(初学必备)
- 2安全资料讲稿
- 3DB11/T 416.2-2007 交通信息广播频道数据格式 第2部分:基于ALER/T-C的定位参考
- 4GB 20229-2006 磷化镓单晶
- 5东方华府悬挑式脚手架搭设施工方案20120630
- 6DZ/T 0171-1997 大比例尺重力勘查规范
- 7隐患排查治理与重大危险源监控技术
- 8NY/T 5288-2006 无公害食品 蛤
- 9基坑护坡工程施工组织设计方案
- 10φ108×1200X36+8辊可调辊筛(套图)
- 11输送机CAD图纸
- 12工艺流程-砂垫层施工工艺流程图
- 13通风与空调设备安装工程检验批质量验收记录表
- 14TB/T 2436-2006 电力牵引 铁路机车车辆和公路车辆用除电子变流器供电的交流电动机之外的旋转电机
- 15模具设计与制造毕业设计(论文)任务书 资料