氧化锆陶瓷基高温自润滑材料
- 文件大小:579.9KB
- 浏览次数:
- 发布时间:2014-03-13
文件介绍:
本资料包含pdf文件1个,下载需要1积分
In order to develop materials with good tribological behavior at a wide temperature range (especially at high temperatures), a series of ZrO2 ( Y2 O3 ) matrix composites which contain various of solid lubricants ( Mo、 MoS2、 BaF2、CaF2、 BaF2/CaF2、 CuO ) were prepared by hot-pressing. Among them, ZrO2 ( Y203 ) - Mo-BaF2/CaF2 composites show low friction coefficient in the range of 800 to 1 000℃. At 1 000℃, the friction coefficient is 0. 28 which is close to the engineering application value. The friction coefficients of the ZrO2( Y203 )-MoSE-CaF2 compos-ites are 0. 30 to 0.20 when sliding against SiC in the range of 800 to 1 000℃. The ZrO2( Y2O3 )-MoS2-CaF2 compos-ites have good friction and wear performance over a wide temperature range. The excellent high-temperature tribologi-cal behavior was mainly attributes to the high-temperature stability of the ZrO2 and the high lubricity of molybdate which formed on the worn surface at high temperature.为了解决较宽温域范围内特别是高温下材料的润滑问题,本文采用热压烧结方法制备了一系列含各种不同固体润滑剂(Mo、MoS2、BaF2、CaF2、BaF2/CaF2、CuO)的氧化锆基高温自润滑陶瓷复合材料。其中ZrO2(Y2O3)-Mo-BaF2/CaF2系列复合物在800~1000℃表现出较低的摩擦因数,在1000℃摩擦因数低至0.28左右,已接近工程应用的许用值;另一种ZrO2(Y2O3)-MoS2-CaF2系列复合物同SiC陶瓷球对磨时在800~1000℃内摩擦因数为0.30~0.22,具有较好的摩擦磨损性能。
文件列表
正在加载...请等待或刷新页面...
发表评论
更多..相关推荐
更多..最近更新
- 1亦庄核心区A座写字楼混凝土工程施工设计方案
- 2建筑工程“四口”及临边防护施工方案
- 3DB33T/724-2008 福寿螺防治技术规范
- 4优路教育《建筑工程管理与实务》冲刺培训讲义
- 5GB/T 31521-2015 公共信息标志 材料、构造和电气装置的一般要求
- 60.4kV低压整套配电系统cad设计图纸
- 7YY/T 0960-2014 脊柱植入物 椎间融合器静态轴向压缩沉陷试验方法
- 8月亮火星的太空飞船inventor设计
- 905SS522_混凝土模块式排水检查井
- 10DB52/T 546-2008 贵州省火力发电企业节能降耗考核及评分标
- 11JB/T 7363-2011 滚动轴承 低碳钢轴承零件碳氮共渗热处理技术条件
- 12半寸阀门中心孔
- 13BS EN 1043-2-1997 金属材料焊接的破坏试验.第2部分:焊接连接件的显微硬度试验
- 14电动自行车组装图CAD图纸
- 15推动架的工艺规程及φ16夹具设计